Effect of brushing simulation on the wear behavior of repaired CAD-CAM restorations.

OBJECTIVE: The aim of the present study was to evaluate the influence of multidirectional brushing on the surface roughness, morphology, and bonding interface of resin-repaired CAD-CAM ceramic and composite restorations. MATERIALS AND METHODS: Twelve (N = 12) blocks (4 mm × 4 mm × 2 mm for parallel axis; 5 mm × 4 mm × 2 mm for perpendicular axis) of lithium disilicate glass-ceramic (IPS e.max CAD, Ivoclar AG) and CAD-CAM resin composite (Tetric CAD, Ivoclar AG) were obtained and repaired with direct resin composite (Clearfil AP-X, Kuraray). An abrasive slurry was prepared and the brushing was performed according to each restorative material and axis of brushing (n = 6; perpendicular to repair interface and parallel to repair interface) during 3,650 cycles (240 strokes per minute) to simulate 3 years of brushing. The surface roughness (Ra) and the profile variation for each material (restoration and direct repair resin composite) were measured at the baseline condition and after brushing, and the mean roughness and presence of steps at the repair interface were evaluated through factorial analysis of Variance (ANOVA). Scanning Electron Microscopy (SEM) images were taken to evaluate the surface topography of the repaired materials after brushing. RESULTS: The mean roughness of the repaired CAD-CAM restorations was affected by the brushing (P < .05), mainly when evaluating the repair material and the interface (P < .05), while the restorative CAD-CAM materials presented more stable values. The profile evaluation showed higher steps at the interface when repairing lithium disilicate than for CAD-CAM resin composite. CONCLUSION: Repaired CAD-CAM restorations were susceptible to wear after brushing simulation. The surface roughness of the direct resin composite was the most affected leading to step development at the interface, particularly in the repaired lithium disilicate samples. Cinical maintenance recalls and polishing protocols must be considered to enhance the longevity of such restorations.

Repair of monolithic zirconia restorations with different direct resin composites: effect on the fatigue bonding and mechanical performance.

OBJECTIVE: The study aims to evaluate the shear bond and flexural strength fatigue behavior of yttrium-stabilized zirconia (4YSZ) repaired using different resin composites. MATERIALS AND METHODS: Cylindric specimens of 4YSZ were obtained for the bond strength (Ø = 6 mm, 1.5 mm of thickness) and biaxial flexural strength (Ø = 15 mm, 1 mm of thickness) fatigue tests and divided into 3 groups according to the repair resin composite: EVO (nanohybrid), BULK (bulk-fill), and FLOW (flowable). The zirconia surface was air-abraded with alumina particles, a 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) primer was applied, and the resin composite was build-up over the zirconia. Fatigue shear bond strength and flexural fatigue strength tests were performed (n = 15). One-way ANOVA and Tukey post hoc tests were carried out for both outcomes, besides scanning electron microscopy and finite element analysis. RESULTS: The repair material affected the fatigue shear bond strength of zirconia ceramic. The BULK group (18.9 MPa) depicted higher bond strength values than FLOW (14.8 MPa) (p = 0.04), while EVO (18.0 MPa) showed similar results to both groups. No effect was observed for the mechanical behavior (p = 0.53). The stress distribution was similar for all groups. CONCLUSION: The repair of yttrium-stabilized zirconia (4YSZ) ceramics with bulk-fill resin composites was the best option for high fatigue bond strength. However, the fatigue mechanical performance was similar regardless of the applied repair material. CLINICAL RELEVANCE: The repair of yttrium-stabilized zirconia (4YSZ) monolithic restorations may be performed with nanohybrid and bulk-fill resin composites in order to promote longevity in the treatment.

Repair protocols for indirect monolithic restorations: a literature review.

Despite the advancements in indirect monolithic restorations, technical complications may occur during function. To overcome this issues, intraoral repair using resin composite is a practical and low-cost procedure, being able to increase the restoration's longevity. This review aimed to evaluate the need for repair and suggest a standardized repair protocol to the main indirect restorative materials. For this, studies were surveyed from PubMed with no language or date restriction, to investigate the scientific evidence of indirect monolithic restoration repair with direct resin composite. A classification to guide clinical decisions was made based on the FDI World Dental Federation criteria about defective indirect restorations considering esthetic and functional standards, along with the patient's view, to decide when polishing, repairing or replacing a defective restoration. Based on 38 surveyed studies, different resin composite intraoral repair protocols, that included mechanical and chemical aspects, were defined depending on the substrate considering resin-based, glass-ceramic or zirconia restorations. The presented criteria and protocols were developed to guide the clinician's decision-making process regarding defective indirect monolithic restorations, prolonging longevity and increasing clinical success.

Cyclic fatigue of a repaired 4 YSZ ceramic: Effect of the repair protocol on the adhesive and mechanical behavior.

Objective: To evaluate the effect of different surface treatments on the morphology, shear bond, and flexural fatigue strength of a repaired translucent zirconia. Methods: Monolithic disc-shaped specimens of translucent zirconia were prepared and ground to simulate repair areas. Four groups underwent different treatments: Air-MDP (air-abrasion with alumina particles and 10-MDP primer), Si-Sil (silica-coated alumina particles with MDP-containing silane), Si-MDP (silica coating with 10-MDP primer), and Uni adhe (universal adhesive). After roughness measurements and treatments, repairs were done using resin composite. Shear bond and flexural (n = 15) fatigue tests were performed. Surface topography, interfacial analysis, fractographic, and finite element analysis were conducted. Results: The zirconia roughness was similar between the groups, however, the surface topography was modified according to the surface treatments. Si-Sil generated higher and more stable bond strength values (20.69 MPa) between translucent zirconia and resin composite when compared to Uni adhe (15.75 MPa) considering the fatigue bond strength scenario, while it was similar to Si-MDP (17.70 MPa) and Air-MDP (18.97 MPa). Regarding the mechanical behavior, Si-Sil (680.83 MPa) also showed higher and significantly different fatigue strength when compared to Uni adhe (584.55 MPa), while both were similar to Si-MDP (634.22 MPa) and Air-MDP (641.86 MPa). Conclusion: The association of mechanical and chemical approaches is essential for long-term bond strength and optimized mechanical behavior, being air-abrasion protocols and the use of silane and/or MDP-based primers suitable for zirconia repair protocols. It was found that relying solely on a universal adhesive was not as effective as other options available. Clinical significance: The surface treatment of repair protocols affects translucent zirconia's morphology. To enhance fatigue behavior in repaired monolithic zirconia, air abrasion is crucial. Exclusive use of a universal adhesive is less effective than other choices. A primer containing silane/MDP holds the potential for stable bond strength and optimized mechanical performance.

Characteristic fatigue strength and reliability of dental glass-ceramics: Effect of distinct surface treatments - Hydrofluoric acid etching and silane treatment vs one-step self-etching ceramic primer.

The aim of this study was to mechanically characterize through flexural fatigue test two CAD-CAM glass-ceramics according to distinct surface etching protocols. To do so, feldspathic (FELD) and lithium disilicate (LD) glass ceramics were subjected to different surface treatments: (1) control - no treatment (Ctrl); (2) conventional protocol etching with 5% hydrofluoric acid followed by silane coupling agent application (HF + SIL; Monobond N, Ivoclar); or (3) using a self-etching ceramic primer (E&P; Monobond Etch & Prime, Ivoclar). Ceramic discs (N = 120; Ø = 12 mm; thickness = 1.2 mm) were produced from CAD-CAM blocks, with 60 being from FELD (VITABLOCS Mark II, Vita Zahnfabrik) and 60 from LD (IPS e.max CAD, Ivoclar). Next, 20 disks of each ceramic were allocated into three groups: Ctrl, HF + SIL, or E&P. Surface roughness data were collected on all samples before and after surface treatments (except for Ctrl). Cyclic fatigue (n = 15) biaxial flexural strength tests were performed by the piston-on-three-balls geometry (ISO 6872) considering the test parameters established from a monotonic test (n = 5). The monotonic test was carried out at a 1 mm/min loading rate and 500 kgf loading cell until fracture to obtain the failure data. The cyclic fatigue test was executed underwater at a frequency up to 20 Hz, with the first stress being 25% of the monotonic test for 5000 cycles, followed by increments of 5% of the monotonic test at each step of 10,000 cycles until failure (fracture). Complementary fractography, topography and Atomic Force Microscopy (AFM) analyses were performed. Characteristic Fatigue Strength (CFS) and Weibull modulus were analyzed by Weibull analysis using the fatigue test data. Roughness and complementary analysis data were analyzed by one-way ANOVA. The statistical results exhibited similar CFS among Ctrl, HF + SIL and E&P for both glass-ceramics. The survival analysis corroborates the findings, however the Weibull modulus pointed out superior structural reliability of FELD treated with the E&P group compared to HF + SIL. According to the complementary analyses, HF + SIL exhibited a higher surface area than E&P and Ctrl for FELD (p = 0.001). Roughness showed statistically significant differences among conditions for FELD (E&P < Ctrl = HF + SIL; p < 0.05) and no difference for LD (p > 0.05). Therefore, the CFS were not influenced by any condition evaluated for FELD and LD glass-ceramics; however, superior structural reliability (higher Weibull modulus) for the feldspathic ceramic treated with the E&P was observed.

Load-bearing capacity under fatigue of bonded-yttria tetragonal zirconia polycrystals and -yttria-stabilized zirconia: Effects of the viscosity of a dual-cured resin cement.

This study aimed to evaluate the effect of low and high viscosities of dual-cured resin cement on the mechanical fatigue behavior of yttria tetragonal zirconia polycrystals (3Y-TZP) and yttria-stabilized zirconia (4YSZ) adhesively luted to a dentin analogue (glass fiber-reinforced epoxy resin). Ceramic discs were randomly divided into four groups (n = 20) based on the following study factors: dual-cured resin cement viscosities (low and high) and zirconia microstructure (3Y-TZP and 4YSZ). The discs were treated by air abrasion with aluminum oxide particles (50 µm), followed by the application of primer, and then luted with high or low viscosity resin cement to the dentin analogue. Subsequently, the luted sets underwent a step-stress fatigue test, which involved an initial load of 200 N, step increments of 100 N, 10,000 cycles per step, and a frequency of 20 Hz. Data on fatigue failure load (FFL) and the number of cycles for failure (CFF) were collected and analyzed using survival tests, including Kaplan-Meier and Mantel-Cox analyses, as well as Weibull analysis. Additionally, topography analysis, fractographic features, bonding interface analysis, and Raman spectroscopy were performed. The results revealed that 3Y-TZP exhibited superior fatigue behavior compared to 4YSZ, regardless of the viscosity of the resin cement used for luting. Among all groups, 3Y-Low exhibited the best fatigue performance, while 4YSZ luted with low or high viscosity resin cements yielded the lowest fatigue behavior (FFL). There were no significant differences in Weibull modulus among the groups. After air abrasion, both ceramics showed similar topography. Raman analysis indicated that the surface of 3Y-TZP ceramics prior to sintering had a monoclinic phase, which transitioned predominantly to tetragonal phase peaks after sintering. A similar transition was observed in 4YSZ ceramics. In summary, 3Y-TZP exhibited superior mechanical fatigue behavior compared to 4YSZ. The influence of resin cement viscosity on fatigue behavior was more pronounced in 3Y-TZP, with low-viscosity resin cement enhancing its performance. However, the mechanical fatigue behavior of 4YSZ was less affected by the viscosity of the dual-cured resin cement, showing similar results with both low and high viscosities. In conclusion, 3Y-TZP demonstrated superior mechanical fatigue behavior compared to 4YSZ. The impact of resin cement viscosity on fatigue behavior was more pronounced in 3Y-TZP, with low-viscosity resin cement enhancing its performance. Conversely, the mechanical fatigue behavior of 4YSZ was less sensitive to the viscosity of the dual-cured resin cement, resulting in similar outcomes with both low and high viscosities.

Mechanical Behavior of Repaired Monolithic Crowns: A 3D Finite Element Analysis.

This study evaluated the mechanical behavior and risk of failure of three CAD-CAM crowns repaired with different resin composites through a three-dimensional (3D) finite element analysis. Three-dimensional models of different cusp-repaired (conventional nanohybrid, bulk-fill, and flowable resin composites) crowns made of zirconia, lithium disilicate, and CAD-CAM resin composite were designed, fixed at the cervical level, and loaded in 100 N at the working cusps, including the repaired one. The models were analyzed to determine the Maximum Principal and Maximum Shear stresses (MPa). Complementary, an in vitro shear bond strength test (n = 10) was performed to calculate the risk of failure for each experimental group. The stress distribution among the models was similar when considering the same restorative material. The crown material affected the stress concentration, which was higher for the ceramic models (±9 MPa for shear stress; ±3 MPa for tensile stress) than for the CAD-CAM composite (±7 MPa for shear stress; ±2 MPa for tensile stress). The shear bond strength was higher for the repaired CAD-CAM resin composite (±17 MPa) when compared to the ceramics (below 12 MPa for all groups), while the repair materials showed similar behavior for each substrate. The stress distribution is more homogenous for repaired resin composite crowns, and a flowable direct resin composite seems suitable to repair ceramic crowns with less risk of failure.

High-versus low-viscosity resin cements: Its effect on the load-bearing capacity under fatigue of a translucent zirconia.

The purpose of the present study was to characterize the elastic modulus and Poisson's ratio of a resin cement with distinct viscosities, and to evaluate their impact on the static and fatigue strength of a translucent zirconia (4Y-PSZ) after air-abrasion surface treatment. Bar-shaped specimens of two different viscosities of resin cement (high and low) were obtained (25 × 10 × 3 mm). Sonelastic and Maxwell principles tests were performed to determine the elastic modulus and Poisson's ratio of each resin cement. Disc-shaped specimens of 4Y-PSZ were made (Ø = 15 mm, 1.2 mm in thickness) for the mechanical tests and allocated into groups according to two factors: surface treatment (presence or absence of air-abrasion with alumina particles; 45 µm grain-size); cement (absence, low or high viscosity). The static (n = 10) and cyclical (n = 15) biaxial flexural strength tests were performed by piston-on-three-balls geometry. A fatigue strength test was executed (20 Hz, initial stress of 60 MPa [12% of the mean static biaxial flexural strength], followed by increments of 25 MPa [5% of the mean static biaxial flexural strength] at each step of 10,000 cycles until the failure). The obtained data were analyzed by Weibull analysis. Survival rates were tabulated by the Kaplan-Meier test. Complementary analyses of surface roughness, topography, cross-sectional interfacial zone, fractography, and zirconia crystalline content (X-ray diffraction) were also performed. The evaluated resin cements with high and low viscosity presented similar elastic modulus (13.63 GPa; 12.74 GPa) and Poisson's ratio (0.32; 0.30), respectively. The air-abraded groups depicted higher mechanical strength of the zirconia ceramics than non-abraded groups (p˂ 0.05), regardless of the resin cement. 4Y-PSZ adhesively bonded to a high or low viscosity resin cement have statistically similar behavior (p˃ 0.05). The mechanical structural reliability of the 4Y-PSZ was not affected by the factors. Therefore, resin cement with high and low viscosity presented similar properties and potential to fill the zirconia surface, and did not affect the mechanical behavior of 4Y-PSZ. However, the air-abrasion surface treatment increased the static and fatigue flexural strength of the translucent zirconia.

Influence of number and position of porcelain specimens in the furnace on flexural strength and translucency

The aim of this study was to investigate the influence of the quantity and positioning of feldspathic ceramic specimens inside the furnace on their flexural strength and translucency. The tested hypotheses were that the arrangement of specimens in the furnance would not influence 1) the translucency or 2) the biaxial strength of the porcelain. Methods: Ninety porcelain specimens were made (1.2 mm thickness and 13.5 mm diameter) and assigned into two main groups (n=15): G1 group - 15 firing cycles containing only one specimen each, always at the center of the refractory; and G5 group - 15 firing cycles containing five specimen each, where one specimen was at the center of the refractory and four specimens positioned equidistantly on the periphery. The translucency test was performed using a spectrophotometer, followed by the flexural strength test, according to ISO 6872:2015. T-student test was performed for both the mechanical and optical obtained data. Results: The flexural strength of the porcelain was not affected by the positioning (center x periphery) of the specimens inside the furnace (p =0.08), but the translucency was affected (periphery > center; p =0.009). Regarding to the number of feldspathic ceramic specimens, the biaxial flexural strength was affected (p =0.025), as well as the translucency (p <0.05). Conclusion: A higher quantity of feldspathic ceramic specimens for each firing cycle decreased its biaxial flexural strength and translucency. Also, specimens positioned at the center of the refractory became less translucent than those positioned at the periphery.

Masking ability of implant abutment substrates by using different ceramic restorative systems.

STATEMENT OF PROBLEM: Information regarding the masking ability of ceramic crowns over different implant abutment materials is scarce. PURPOSE: The purpose of this in vitro study was to evaluate the masking ability of different monolithic or bilayer ceramic materials with different thicknesses over substrates indicated for implant restorations by using opaque and translucent evaluation pastes. MATERIAL AND METHODS: Disk-shaped specimens, shade A1 (VITA Classic; Ø10×1.5 to 2.5 mm), of different ceramics (a bilayer system [yttria-stabilized zirconia infrastructure+porcelain veneer: Zir+Pc] and monolithic systems [lithium disilicate under low, medium, or high translucency: LtLD, MtLD, or HtLD, respectively, and a high-translucent yttria-stabilized zirconia: HtZir]) were made (n=4). The color difference (ΔE00) was assessed by using the CIEDE2000 formula and considering the different ceramic systems over 5 implant abutment materials (A1 shade Zir [Zir A1]; white Zir [White Zir]; A1 low-translucency lithium disilicate [LD]; polyetheretherketone [PEEK]; and titanium [Ti]) when using 2 different evaluation pastes (translucent or opaque). The control comparison was the restorative material positioned over the Zir A1 substrate with a translucent evaluation paste. Statistical analysis was made by using a 2-way ANOVA and Tukey post hoc tests (α=.05) for ΔE00 data considering the restorative material and luting agent factors as their association. Additionally, ΔE00 data were qualitatively analyzed considering the acceptability and perceptibility thresholds. The translucency parameter (TP00) of each restorative material was evaluated, and data were submitted to 1-way ANOVA and Tukey post hoc tests (α=.05). RESULTS: The most predictable masking ability was seen with Zir+Pc regardless of the evaluation paste used. Nevertheless, under 1.5-mm thickness, Zir+Pc did not adequately mask Ti (ΔE00>1.77). Most monolithic ceramics did not mask discolored substrates (PEEK or Ti, ΔE00>1.77). The exception was HtZir, which presented acceptable masking ability over PEEK at 2.5-mm thickness with both evaluation pastes (ΔE00<1.77). Regardless of the restorative material thickness, Zir+Pc showed the lowest (P<.05) TP00 values (TP00=3.45 at 1.5-mm thickness; TP00=2.00 at 2.5-mm thickness), and HtLD presented the highest (P<.05, TP00=23.50 at 1.5-mm thickness; TP00=13.36 at 2.5-mm thickness). HtZir showed similar TP00 to MtLD at 1.5-mm thickness and similar TP00 to Zir+Pc when used at 2.5-mm thickness (P>.05). CONCLUSIONS: Monolithic ceramics should be used with caution over discolored implant abutments. Bilayer systems (Zir+Pc) were the most predictable approach to adequately masking discolored substrates such as PEEK or Ti. An increased restoration thickness provided higher masking ability for all restorative materials tested.

Simulation of CAD/CAM milling on lithium disilicate: Mechanical and topographic analyses of surface grinding different protocols.

The aim of this study was to evaluate the topography and the fatigue performance of lithium disilicate glass-ceramic after surface grinding through different laboratory protocols used to simulate the Computer-aided design/Computer-aided manufacturing (CAD/CAM) milling. Ceramic discs (IPS e.max CAD, Ø = 13.5 mm × 1.2 mm of thickness) were produced through different methodologies: milling in CAD/CAM system (CAD/CAM group); produced in-lab with a polished surface (POL group); or produced through in-lab methods and randomly distributed into five groups according to different grinding protocols to simulate the CAD/CAM milling [grinding with a CAD/CAM bur coupled to a mandrel (CAD/CAM Bur group); fine diamond bur using oscillatory movements (DBO group); fine diamond bur in x and y axes of the disc (DBXY group); #60-grit silicon carbide sandpaper (SiC group); and #60-grit wood sandpaper (WS group)]. The specimens were fatigue tested (n = 15) according to the step-stress method (initial load: 60 N; step-size: 20 N; 10,000 cycles/step; 20 Hz frequency). A roughness analysis was performed on all specimens, while fractal dimension (FD) and fractography were performed on representative samples. The Kaplan-Meier analysis showed that the POL (293.3 N) group presented better fatigue performance (higher load and number of cycles for failure) (p < 0.05) than the other groups (CAD/CAM = 222.7 N; CAD/CAM Bur = 181.3 N; DBO = 184.0 N; DBXY = 192.0 N; SiC = 182.6 N; WS = 182.6 N). For roughness, only the SiC (Ra = 1.616; Rz = 10.465) and WS (Ra = 1.673; Rz = 10.655) groups produced statistically similar Ra (µm) and Rz (µm) values to the CAD/CAM (Ra = 1.628; Rz = 9.571) group (p > 0.05). The surface created by CAD/CAM milling and POL group exhibited more complexity (FD) higher values than the experimental groups. For the ceramic surface topography images, the CAD/CAM milling visibly produced a uniform surface compared to the other groups; however, the POL group was the smoothest. The DBO, DBXY, SiC, and WS groups resulted in similar characteristics of surface topography. Therefore, although the SiC and WS groups showed similar roughness to the control group (CAD/CAM), no in-lab simulation method was fully capable to mimic the mechanical performance of the CAD/CAM-milled lithium disilicate glass-ceramic.

Surface Treatments and Adhesives Used to Increase the Bond Strength Between Polyetheretherketone and Resin-based Dental Materials: A Scoping Review.

PURPOSE: To identify and discuss the available surface treatments and adhesives for polyetheretherketone (PEEK) to increase its bond strength to resin-based materials used in dentistry. MATERIALS AND METHODS: The reporting of this scoping review was based on PRISMA. The study protocol was made available at: https://osf.io/4nur9/. Studies which evaluated PEEK surface treatments and its bond strength to resin-based materials were selected. The search was performed in PubMed, Scopus, Web of Sciences and Cochrane databases. The screening was undertaken by 3 independent researchers using the Rayyan program. A descriptive analysis was performed considering study characteristics and main findings (title, data of publication, authors, PEEK characteristics, surface treatments, control group, bonded set, luting agent, specimen geometry, storage, thermocycling, pre-test failures, test geometry, failure analysis, main findings, and compliance with normative guidelines). RESULTS: The initial search yielded 1965 articles, of which 32 were included for descriptive analysis. The review showed that the use of surface treatments and adhesives are important to promote bond strength to PEEK. Up until now, various surface treatments have been explored for bond improvement to PEEK. Sulfuric acid etching is commonly reported as promoting the highest bond strength, followed by alumina-particle air abrasion. Regarding adhesives, the use of a specific adhesive containing MMA, PETIA (pentaerythritol triacrylate), and dimethacrylates yields the best adhesive performance. CONCLUSION: Sulfuric acid etching and alumina particle air abrasion followed by application of bonding agents containing MMA, PETIA and dimethacrylates are the most effective choices to increase resin-based materials' adhesion to PEEK.

Does Adhesive Luting Reinforce the Mechanical Properties of Dental Ceramics Used as Restorative Materials? A Systematic Review and Meta-Analysis.

PURPOSE: This systematic review aims to explore and compile the effect of adhesive luting on the mechanical properties of dental ceramics used as restorative materials. MATERIALS AND METHODS: The PubMed/MEDLINE, Web of Science and Scopus databases were searched on January 31st, 2021 to select laboratory studies written in English, without publishing-date restrictions, which compared the mechanical properties of commercially available dental ceramics as restorative materials luted using adhesive vs non-adhesive strategies. A total of 20 (out of 2039) studies were eligible and included in the analysis. Two authors independently selected the studies, extracted the data and assessed the risk of bias. Mean differences (RevMan5.1, random effects model, α = 0.05) were obtained by comparing resistance values of adhesive and non-adhesive conditions (global analysis). Subgroup analyses were performed considering ceramic composition and aging. RESULTS: In the global analysis, adhesive luting induced higher mechanical resistance values compared to non-adhesive luting (p ≤ 0.01). The same effect was observed for glass and alumina ceramics (p ≤ 0.01), but not for zirconia polycrystals (p = 0.83). Adhesive luting was favorable in both the aged and non-aged subgroup analysis (p ≤ 0.01). High heterogeneity was found in all meta-analyses. All analyzed studies in the systematic review scored negatively for risk of bias in most of the factors considered. CONCLUSIONS: Adhesive luting reinforces the mechanical properties of dental ceramics used as restorative materials, with the exception of zirconia polycrystals.

Effect of immediate dentin sealing and temporary cement removal on bond strength of resin cements to dentin / Efeito do selamento dentinário imediato e da remoção do cimento provisório na resistência de união de cimentos resinosos à dentina

Objective: To evaluate the influence of immediate dentin sealing (IDS) and mechanical methods for removing the temporary cement on the bond strength between dentin and resin cements. Material and Methods: Bovine incisors were ground until dentin exposure and divided according to two factors: "dentin surface treatment"' - cleaning with manual dental excavator (DE), with Robinson bristle brush and pumice paste (PP) or IDS application with Single Bond 2 (IDS/SB+PP) or Single Bond Universal (IDS/SBU+PP) plus cleaning with PP; and "resin cement" - Self-adhesive (RelyX U200) or conventional cement with self-etching adhesive (Multilink Automix). Simulating provisional restoration, acrylic resin plates were cemented onto the dentin surface (with or without IDS) with a non-eugenol temporary cement, and stored in distilled water (37 ºC; 7 days). The acrylic plates were removed, the dentin surface was cleaned (PP or DE), and starch tubes were positioned on the dentin where the resin cements were applied. After 24 h, the specimens were submitted to a microshear test (wire-loop method). Results: Two-way analysis of variance showed statistically significant influence of dentine surface treatments (p< 0.001) and resin cement (p= 0.001) in the bond strength values. The IDS/SBU+PP/U200 (7.24 MPa) and IDS/SBU+PP/MULTI (6.40 MPa) groups presented higher values when compared to cleaning with DE (DE/U200= 4.60 MPa; DE/MULTI= 1.45 MPa) and PP (PP/U200= 3.74 MPa; PP/MULTI= 3.14 MPa). Statistical difference was also found between the cements when dental excavator treatment was used (RelyX U200 ˃ Multilink Automix). The IDS/SBU+PP protocol presented a higher percentage of cohesive failures. The micrographs showed differences in dentin surface characteristics among the groups. Conclusion: Immediate dentin sealing increased the bond strength of the resin cements to dentin compared to mechanical cleaning only, regardless the resin cement. (AU)

Objetivo: Avaliar a influência do selamento dentinário imediato (IDS) e dos métodos mecânicos de remoção do cimento provisório na resistência de união entre dentina e cimentos resinosos. Materiais e Métodos: Incisivos bovinos foram desgastados até a exposição da dentina e divididos de acordo com dois fatores: "tratamento da superfície dentinária" - limpeza com cureta dentária manual (DE), com escova de cerdas Robinson e pasta de pedra-pomes (PP) ou aplicação de IDS com Single Bond 2 (IDS/SB +PP) ou Single Bond Universal (IDS/SBU+PP) mais limpeza com PP; e "cimento resinoso" - autoadesivo (RelyX U200) ou cimento convencional com adesivo autocondicionante (Multilink Automix). Simulando a restauração provisória, placas de resina acrílica foram cimentadas na superfície dentinária (com ou sem IDS) com um cimento provisório sem eugenol e armazenadas em água destilada (37 ºC; 7 dias). As placas de acrílico foram removidas, a superfície dentinária foi limpa (PP ou DE) e tubos de amido foram posicionados na dentina onde os cimentos resinosos foram aplicados. Após 24 h, os corpos-de-prova foram submetidos ao ensaio de microcisalhamento (método wire-loop). Resultados: A análise de variância de dois fatores mostrou influência estatisticamente significativa dos tratamentos de superfície dentinária (p< 0,001) e cimento resinoso (p= 0,001) nos valores de resistência de união. Os grupos IDS/SBU+PP/U200 (7,24 MPa) e IDS/SBU+PP/MULTI (6,40 MPa) apresentaram valores maiores quando comparados à limpeza com DE (DE/U200= 4,60 MPa; DE/MULTI= 1,45 MPa) e PP (PP/U200= 3,74 MPa; PP/MULTI= 3,14 MPa). Uma diferença estatística também foi encontrada entre os cimentos quando o tratamento com cureta dentária foi usado (RelyX U200 ˃ Multilink Automix). O protocolo IDS/SBU+PP apresentou maior percentual de falhas coesivas. As micrografias mostraram diferenças nas características da superfície dentinária entre os grupos. Conclusão: O selamento dentinário imediato aumentou a resistência de união dos cimentos resinosos à dentina em comparação com a limpeza mecânica apenas, independentemente do cimento resinoso.(AU)

The influence of roughness on the resistance to impact of different CAD/CAM dental ceramics

Abstract This study aimed to investigate the effect of surface roughness (polished vs. CAD/CAM milling simulation) on impact strength of five dental ceramics for manufacturing CAD/CAM monolithic restorations. Specimens of five ceramics (FC- feldspathic glass-ceramic; PICN- polymer-infiltrated ceramic-network; ZLS- zirconia-reinforced lithium silicate glass-ceramic; LD- lithium disilicate glass-ceramic; YZ- yttria-stabilized tetragonal zirconia polycrystal ceramic) to be tested under impact (15×10×2mm3; n= 15) were divided into two groups, according to surface treatment: polishing (pol) and grinding (gri) as CAD/CAM milling simulation. Impact strength was tested using the Dynstat method. Roughness, topographic, fractographic and finite element analyses were performed. The impact strength data were analyzed by Weibull, and Pearson correlation was used to correlate roughness and impact strength data. The CAD/CAM milling simulation led to significantly (p<0.05) greater roughness (Ra and Rz) and statistically reduced the impact strength for PICN (polPICN= 4.59 to griPICN= 1.09; ±76% decrease), for LD (polLD= 17.69 to griLD= 10.09; ±43% decrease) and for YZ (polYZ= 74.99 to griYZ= 20.67; ±72% decrease) ceramics; and also promoted a more irregular topography with scratches and grooves. Fractographic and FEA analyses depicted the origin of failure at the higher stress concentration side during the impact test, where the pendulum impacted. The CAD/CAM milling simulation significantly decreased the impact strength of the evaluated ceramic materials.

Resumo Este estudo teve como objetivo investigar o efeito da rugosidade da superfície (polido vs. simulação da usinagem em CAD/CAM) na resistência ao impacto de cinco cerâmicas odontológicas indicadas na fabricação de restaurações monolíticas em CAD/CAM. Espécimes de cinco cerâmicas (FC- vitrocerâmica feldspática; PICN- rede de cerâmica infiltrada com polímero; ZLS- vitrocerâmica de silicato de lítio reforçada com zircônia; LD- vitrocerâmica de dissilicato de lítio; YZ- cerâmica policristalina de zircônia tetragonal estabilizada com ítria), a serem testados sob impacto (15 × 10 × 2mm3; n= 15), foram divididos em dois grupos, de acordo com o tratamento superficial: polimento (pol) e desgaste (gri), usado como simulação da usinagem em CAD/CAM. A resistência ao impacto foi testada usando o método Dynstat. Foram realizadas as análises de rugosidade, topografia, fractografia e análise de elementos finitos. Os dados de resistência ao impacto foram analisados pela análise de Weibull, e a correlação de Pearson foi usada para correlacionar os dados de rugosidade e resistência ao impacto. A simulação da usinagem em CAD/CAM levou a uma rugosidade (Ra e Rz) significativamente maior (p < 0,05) para todas as cerâmicas, e reduziu estatisticamente a resistência ao impacto para as cerâmicas PICN (polPICN = 4,59 para griPICN = 1,09; redução de ± 76%), LD (polLD = 17,69 para griLD = 10,09; ± 43% de redução) e YZ (polYZ = 74,99 para griYZ = 20,67; ± 72% de redução); e também promoveu uma topografia mais irregular apresentando riscos e sulcos acentuados. As análises de fractografia e de elementos finitos mostraram a origem da falha no lado de maior concentração de tensão durante o teste de impacto, onde o pêndulo impactou o espécime. A simulação da usinagem em CAD/CAM reduziu significativamente a resistência ao impacto dos materiais cerâmicos avaliados.

Load-bearing capacity under fatigue and FEA analysis of simplified ceramic restorations supported by Peek or zirconia polycrystals as foundation substrate for implant purposes.

The fatigue behavior and FEA analysis of different ceramic materials cemented over distinct substrates for implant-supported crowns were evaluated in this study. Discs of 10 mm in diameter of both restorative and substrate materials were made and randomly allocated into pairs (n = 15) considering the two study factors: 'restorative ceramic material' (1 mm thickness) - polymer-infiltrated ceramic network (PICN), lithium disilicate (LD), zirconia-reinforced lithium silicate (ZLS), or translucent zirconia (TZ); and 'foundation substrate' (2 mm thickness) - polyetheretherketone (Peek) or yttrium-stabilized zirconia (YZ). Adhesive cementation was made with a dual cure resin cement. Fatigue testing was run using the step-stress methodology: initial load of 200 N for 5000 cycles, followed by steps of 10,000 cycles starting at 400 N up to 2800 N or until failure, step size of 200 N, frequency of 20 Hz. Data were analyzed by the Kaplan Meier and log-rank post-hoc tests. Fractography analysis (stereomicroscope and SEM) and FEA were also performed. Both factors under study and their interaction statistically influenced the fatigue failure load (FFL), cycles for failure (CFF) and survival rates (p < 0.001). The restorative materials bonded to YZ had higher FFL and CFF than when adhering to Peek, while restorative materials with more crystalline content (TZ and ZLS) showed higher FFL and CFF than LD and PICN. The fractography analysis showed that all materials bonded to YZ resulted in failures starting at the occlusal surface (Hertzian cone cracks), while materials bonded to Peek had radial cracks from the ceramic-cement intaglio surface. FEA analysis showed that tensile stress concentration decreased in the intaglio surface when testing the restorative material over a stiffer (YZ) foundation substrate. In addition, the higher the restorative material's crystalline content, the more the stress is concentrated within the material (TZ > ZLS ≥ LD > PICN) when bonded to the same foundation substrate. Thus, it concluded that a stiffer foundation substrate (YZ) enhances the load-bearing capacity under fatigue of the restorative set; that restorative materials with higher crystalline content results in higher fatigue performance of the set, regardless of the foundation used; and that the foundation material influences the failure pattern of the restorative set.

In-lab simulation of CAD/CAM milling of lithium disilicate glass-ceramic specimens: Effect on the fatigue behavior of the bonded ceramic.

The aim of this study was to evaluate the effect of in-lab simulation procedures performed on a lithium disilicate ceramic luted to a dentin-analogue material regarding the fatigue performance and topographic changes. Lithium disilicate ceramic (IPS e.max CAD) discs (Ø = 13.5 mm and 1.5 mm of thickness) were produced in different ways: milled in a CAD/CAM system (CAD/CAM - control group); mirror-polished (POL group); produced in-lab and ground with #60 silicon carbide paper (SiC group); with #60 wood sandpaper (WS group); with a fine diamond bur (DB group); or with a CAD/CAM bur adapted in a handpiece with a custom mandrel (MANDREL group). The ceramic discs were adhesively luted (Multilink N) onto dentin analogue discs (Ø = 12 mm and 2 mm of thickness) and fatigue testing (n = 19 discs) was performed by step-stress methodology (initial load of 200 N; step-size of 50 N; 10,000 cycles per step; 20 Hz). Surface roughness and contact angle analysis were also performed. According to Kaplan-Meier and post-hoc Mantel-Cox (log-rank), distinct fabrication methods affected the fatigue performance of bonded glass-ceramic discs (p< 0.001). The CAD/CAM group presented the lowest fatigue failure loads (1250 N) and number of cycles for failure (185,000), while the POL groups obtained the highest results (1752 N; 284,444 cycles). The in-lab groups had intermediate values (1355 - 1526 N; 206,052 - 238,684 cycles). Polished specimens presented the lowest roughness values (Ra = 0.041 µm), while the SiC (1.604 µm), WS (1.701 µm), and MANDREL (1.867 µm) groups showed statistically similar roughness values to the CAD/CAM group (1.738 µm). Despite differences before etching, the contact angle was similar among the milled and simulated groups after etching, except for the polished group. Even with some topographic similarities, the tested in-lab simulation methods were not able to mimic the milled specimens in terms of fatigue findings, leading to distinct magnitude of overestimations of the results.

Surface treatments and its effects on the fatigue behavior of a 5% mol yttria partially stabilized zirconia material.

This study evaluated the effect of distinct surface treatments on the fatigue behavior (biaxial flexural fatigue testing) and surface characteristics (topography and roughness) of a 5% mol yttria partially stabilized zirconia ceramic (5Y-PSZ). Disc-shaped specimens of 5Y-PSZ (IPS e.max ZirCAD MT Multi) were manufactured (ISO 6872-2015) and allocated into six groups (n = 15) considering the following surface treatments: Ctrl - no-treatment; GLZ - low-fusing porcelain glaze application; SNF - 5 nm SiO2 nanofilm; AlOx - aluminum oxide particle air-abrasion; SiC - silica-coated aluminum oxide particles (silica-coating); and 7%Si - 7% silica-coated aluminum oxide particles (silica-coating). The biaxial flexural fatigue tests were performed by the step-stress method (20Hz for 10,000 cycles) with a step increment of 50N starting at 100N and proceeding until failure detection. The samples were tested with the treated surface facing down (tensile stress side). Topography, fractography, roughness, and phase content assessments of treated specimens were performed. GLZ group presented the highest fatigue behavior, while AlOx presented the lowest performance, and was only similar to SiC and 7%Si. Ctrl and SNF presented intermediary fatigue behavior, and were also similar to SiC and 7%Si. GLZ promoted a rougher surface, Ctrl and SNF had the lowest roughness, while the air-abrasion groups presented intermediary roughness. No m-phase content was detected (only t and c phases were detected). In conclusion, the application of a thin-layer of low-fusing porcelain glaze, the deposition of silica nanofilms and the air-abrasion with silica-coated alumina particles had no detrimental effect on the fatigue behavior of the 5Y-PSZ, while the air-abrasion with alumina particles damaged the fatigue outcomes.

Different Etching Times of a One-step Ceramic Primer: Effect on the Resin Bond Strength Durability to a CAD/CAM Lithium-Disilicate Glass-Ceramic.

PURPOSE: To evaluate the effect of different etching times of a self-etching ceramic primer on the microshear bond strength (µSBS) and topographic surface pattern of a lithium-disilicate glass-ceramic. MATERIALS AND METHODS: Ceramic slices were subjected to an in-lab simulation of CAD/CAM milling and randomly allocated to 10 groups (n = 35) considering two factors: "surface treatment" in 5 levels - one control group (5% hydrofluoric acid + silane application [HF5+SIL]), and 4 experimental groups using ceramic etching/primer (Monobond Etch & Prime, E&P) with different passive application times (40 s, 2 min, 5 min, or 10 min); and "aging" factor in 2 levels - short-term (after 24 h), or long-term (storage for 180 days + 12,000 thermal cycles). Composite cement cylinders were built and µSBS tests were run in a universal testing machine. The failure patterns were categorized, and complementary analyses with SEM and Atomic Force Microscopy (AFM) were performed. RESULTS: The groups showed statistically similar bond strengths in the short term (range 22.4 to 25.1 MPa). However, only the E&P 20s+40s (19.3 MPa) and E&P 20s+5min (21.5 MPa) groups maintained stable bond strength in the long term, and HF5+SIL (17.1 MPa) presented statistically significantly lower values than did E&P 20s+5min. The failure pattern was predominantly adhesive. The increased application time of the ceramic primer promoted greater dissolution of the glass matrix; thus, the E&P 20s+10min group presented the most complex surface characteristics in the fractal dimension analysis. CONCLUSION: The self-etching ceramic primer can be used as an alternative to classical conditioning with HF plus silane, promoting stable bond strength for etching times of 40 s or 5 min of passive application.

The influence of roughness on the resistance to impact of different CAD/CAM dental ceramics.

This study aimed to investigate the effect of surface roughness (polished vs. CAD/CAM milling simulation) on impact strength of five dental ceramics for manufacturing CAD/CAM monolithic restorations. Specimens of five ceramics (FC- feldspathic glass-ceramic; PICN- polymer-infiltrated ceramic-network; ZLS- zirconia-reinforced lithium silicate glass-ceramic; LD- lithium disilicate glass-ceramic; YZ- yttria-stabilized tetragonal zirconia polycrystal ceramic) to be tested under impact (15×10×2mm3; n= 15) were divided into two groups, according to surface treatment: polishing (pol) and grinding (gri) as CAD/CAM milling simulation. Impact strength was tested using the Dynstat method. Roughness, topographic, fractographic and finite element analyses were performed. The impact strength data were analyzed by Weibull, and Pearson correlation was used to correlate roughness and impact strength data. The CAD/CAM milling simulation led to significantly (p<0.05) greater roughness (Ra and Rz) and statistically reduced the impact strength for PICN (polPICN= 4.59 to griPICN= 1.09; ±76% decrease), for LD (polLD= 17.69 to griLD= 10.09; ±43% decrease) and for YZ (polYZ= 74.99 to griYZ= 20.67; ±72% decrease) ceramics; and also promoted a more irregular topography with scratches and grooves. Fractographic and FEA analyses depicted the origin of failure at the higher stress concentration side during the impact test, where the pendulum impacted. The CAD/CAM milling simulation significantly decreased the impact strength of the evaluated ceramic materials.